如何弯曲 ABS 板

How bends ABS boards

用吹风机加热后即可弯曲。ABS 板材极好的冲击强度、尺寸稳定性好、染色性、

成型加工和机械加工好、高机械强度、高刚度、低吸水性、耐腐蚀性好、连接简

单、无毒无味、具有优良的化学性能和电气绝缘性能。abs 板材能耐热不变形,

在低温条件下也具有高抗冲击韧性。还是一种坚硬，不易划伤，不易形变的材料。

低吸水性；高尺寸稳定性。常规 ABS 板不是很白，但韧性非常好，可以用剪板

机裁剪，也可开模具冲。

Yangzhou Zhuotai New Material Co., Ltd. tells you that it can be bent

after heating with a hair dryer. ABS sheet has excellent impact strength,

good dimensional stability, dyeability, good molding and machining,

high mechanical strength, high stiffness, low water absorption, good

corrosion resistance, simple connection, non-toxic and tasteless, and has

excellent chemical properties performance and electrical insulation

properties. ABS sheets can withstand heat without deformation, and also

have high impact resistance and toughness under low temperature

conditions. It is also a hard material that is not easily scratched or

deformed. Low water absorption; high dimensional stability.

Conventional ABS boards are not very white, but have very good

toughness. They can be cut with a shearing machine or punched with a

mold.

ZOYAABS 片材,PP 片材,PE 片材选扬州卓泰新材料有限公司。

Choose ABS sheets, PP sheets, and PE sheets from Yangzhou Zhuotai

New Materials Co., Ltd.

ZOYA

如何给聚乙烯板材去胶

How to remove glue from polyethylene sheets

扬州卓泰新材料有限公司在近几年内板材行业不断发展的形式下，对于聚乙烯板材的生产

也已经成为各大行业中普遍采用的板材之一，其超高性能得到了广大用户的普遍认可，在应

用一段时间后可能会出现脱胶的现象，这时就需要施工人员在施工完毕后把保护层从聚乙烯

板材上撕下来的时候，粘胶会有一些被留在了板材产品上，造成美观度下降。如何去除聚乙

烯板材上的粘胶一直是人们很头疼的问题，对此为了更好的帮助到大家，专业技术人员对其

去除方法介绍如下：

With the continuous development of the panel industry in recent years, Yangzhou

Zhuotai New Materials Co., Ltd. has become one of the panels commonly used in

various major industries for the production of polyethylene panels. Its ultra-high

performance has been generally recognized by the majority of users. , the

phenomenon of degumming may occur after a period of application. In this case,

when the construction workers tear off the protective layer from the polyethylene

sheet after construction, some of the adhesive will be left on the sheet product,

causing Decreased aesthetics. How to remove the adhesive on polyethylene sheets

has always been a headache for people. In order to better help everyone,

professional technicians introduce the removal methods as follows:

若想要去除超高分子量聚乙烯板材上的粘胶，可以使用脱胶清洗剂清洗，清洗后的板材光滑

无胶痕、无煤油味，并且该工艺过程简单，成本低，能全面提高劳动生产率，降低费用，无

环境污染。

If you want to remove the adhesive on ultra-high molecular weight polyethylene

ZOTAsheets, you can use a degumming cleaning agent to clean them. The cleaned

sheets will be smooth and have no glue marks or kerosene smell. Moreover, this

process is simple and low-cost, and can comprehensively improve labor

productivity. Reduce costs and no environmental pollution.

有关对于聚乙烯板材上粘胶的去除方法，暂时为大家介绍到这里，只有我们对其做好日常维

护及清洁工作，才能够确保对其应用更加长久。

Regarding the removal method of adhesive on polyethylene sheets, we will

temporarily introduce it to you here. Only if we do daily maintenance and cleaning

work can we ensure that it can be used for a longer period of time.

ZOTA

ABS 材质的相关问题

Issues related to ABS material

ABS 塑料是丙烯腈(A)-丁二烯(B)-苯乙烯(S)的三元共聚物。它综合了三种组分的

性能，其中丙烯腈具有高的硬度和强度、耐热性和耐腐蚀性；丁二烯具有抗冲击

性和韧性；苯乙烯具有表面高光泽性、易着色性和易加工性。上述三组分的特性

使 ABS 塑料成为一种“质坚、性韧、刚性大”的综合性能良好的热塑性塑料。

调整 ABS 三组分的比例，其性能也随之发生变化，以适应各种应用的要求，如

高抗 ABS、耐热 ABS、高光泽 ABS 等。ABS 塑料的成型加工性好，可采用注射、

挤出、热成型等方法成型，可进行锯、钻、锉、磨等机械加工，可用三氯甲烷等

有机溶剂粘接，还可进行涂饰、电镀等表面处理。ABS 塑料还是理想的木材代

用品和建筑材料等。ABS 塑料强度高，轻便，表面硬度大，非常光滑，易清洁

处理，尺寸稳定，抗蠕变性好，宜作电镀处理材料。其应用领域仍在不断扩大。

ABS 塑料在工业中应用极为广泛。ABS 注射制品常用来制作壳体、箱体、零部

件、玩具等。挤出制品多为板材、棒材、管材等，可进行热压、复合加工及制作

模型。

塑料 ABS 树脂是产量最大，应用最广泛的聚合物，它将 PB，PAN，PS 的各种

性能有机地统一起来，兼具韧，硬，刚相均衡的优良力学性能。ABS 是丙烯腈、

丁二烯和苯乙烯的三元共聚物，A 代表丙烯腈，B 代表丁二烯，S 代表苯乙烯。

经过实际使用发现：ABS 塑料管材，不耐硫酸腐蚀，遇硫酸就粉碎性破裂。

由于具有三种组成，而赋予了其很好的性能；丙烯腈赋予 ABS 树脂的化学稳定

性、耐油性、一定的刚度和硬度；丁二烯使其韧性、冲击性和耐寒性有所提高；

ZOTA苯乙烯使其具有良好的介电性能，并呈现良好的加工性。

大部分 ABS 是无毒的，不透水，但略透水蒸气，吸水率低，室温浸水一年吸水

率不超过 1%而物理性能不起变化。ABS 树脂制品表面可以抛光，能得到高度光

泽的制品。比一般塑料的强度高 3-5 倍。

ABS 具有优良的综合物理和机械性能，较好的低温抗冲击性能。尺寸稳定性。

电性能、耐磨性、抗化学药品性、染色性、成品加工和机械加工较好。ABS 树

脂耐水、无机盐、碱和酸类，不溶于大部分醇类和烃类溶剂，而容易溶于醛、酮、

酯和某些氯代烃中。ABS 树脂热变形温度低可燃，耐热性较差。熔融温度在

217~237℃，热分解温度在 250℃以上。如今的市场上改性 ABS 材料，很多都

是掺杂了水口料、再生料。导致客户成型产品性能不是很稳定。

（

1）物料性能

综合性能较好，冲击强度较高，化学稳定性，电性能良好；

与 372 有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理；

有高抗冲、高耐热、阻燃、增强、透明等级别；

流动性比 HIPS 差一点，比 PMMA、PC 等好，柔韧性好；

适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件。

（

2）成型性能

无定形材料，流动性中等，吸湿大，必须充分干燥，表面要求光泽的塑件须长时

间预热干燥 80-90 度，3 小时；

宜取高料温，高模温，但料温过高易分解(分解温度为>270℃)。对精度较高的

塑件，模温宜取 50-60℃，对高光泽、耐热塑件，模温宜取 60-80℃；

如需解决夹水纹，需提高材料的流动性，采取高料温、高模温，或者改变入水位

ZOTA等方法；

如成形耐热级或阻燃级材料，生产 3-7 天后模具表面会残存塑料分解物，导致模

具表面发亮，需对模具及时进行清理，同时模具表面需增加排气位置；

冷却速度快，模具浇注系统应以粗，短为原则，宜设冷料穴，浇口宜取大，如：

直接浇口，圆盘浇口或扇形浇口等，但应防止内应力增大，必要时可采用调整式

浇口。模具宜加热，应选用耐磨钢；

料温对塑件质量影响较大，料温过低会造成缺料，表面无光泽，银丝紊乱料温过

高易溢边，出现银丝暗条，塑件变色起泡；

模温对塑件质量影响很大，模温低时收缩率，伸长率，抗冲击强度大，抗弯，抗

压，抗张强度低。模温超过 120℃时，塑件冷却慢，易变形粘模，脱模困难，成

型周期长；

成型收缩率小，易发生熔融开裂，产生应力集中，故成型时应严格控制成型条件，

成型后塑件宜退火处理；

熔融温度高，粘度高，对剪切作用不敏感，对大于 200 克的塑件，应采用螺杆

式注射机，喷嘴应加热，宜用开畅式延伸式喷嘴，注塑速度中高速。

ABS plastic is a terpolymer of acrylonitrile (A)-butadiene (B)-styrene (S).

It combines the properties of three components, among which

acrylonitrile has high hardness and strength, heat resistance and

corrosion resistance; butadiene has impact resistance and toughness;

styrene has high surface gloss, easy coloring and Ease of processing. The

characteristics of the above three components make ABS plastic a

thermoplastic with good comprehensive properties that is “hard, tough

ZOTAand rigid”. By adjusting the proportion of the three components of ABS,

its performance will also change to adapt to the requirements of various

applications, such as high-resistant ABS, heat-resistant ABS, high-gloss

ABS, etc. ABS plastic has good molding processability and can be formed

by injection, extrusion, thermoforming and other methods. It can be

processed by sawing, drilling, filing, grinding and other mechanical

processes. It can be bonded with organic solvents such as chloroform,

and can also be painted and electroplated. and other surface treatments.

ABS plastic is also an ideal wood substitute and building material. ABS

plastic has high strength, light weight, high surface hardness, very

smooth, easy to clean, dimensional stability, good creep resistance, and

is suitable for electroplating processing materials. Its application areas

are still expanding. ABS plastic is widely used in industry. ABS injection

products are commonly used to make casings, boxes, parts, toys, etc.

Extruded products are mostly plates, rods, pipes, etc., which can be

hot-pressed, compounded, and modeled.

Plastic ABS resin is the polymer with the largest output and the most

widely used. It organically unifies the various properties of PB, PAN, and

PS, and has excellent mechanical properties with a balance of toughness,

hardness, and rigidity. ABS is a terpolymer of acrylonitrile, butadiene and

styrene, A represents acrylonitrile, B represents butadiene, and S

represents styrene. After actual use, it was found that ABS plastic pipes

ZOTAare not resistant to sulfuric acid corrosion and will shatter when exposed

to sulfuric acid.

Because it has three components, it gives it good performance;

acrylonitrile gives ABS resin chemical stability, oil resistance, certain

stiffness and hardness; butadiene improves its toughness, impact

resistance and cold resistance; Styrene gives it good dielectric properties

and exhibits good processability.

Most ABS is non-toxic and impermeable to water, but is slightly

permeable to water vapor and has a low water absorption rate. The water

absorption rate does not exceed 1% in one year when soaked in water at

room temperature without any change in physical properties. The

surface of ABS resin products can be polished to obtain highly glossy

products. It is 3-5 times stronger than ordinary plastic.

ABS has excellent comprehensive physical and mechanical properties

and good low-temperature impact resistance. Dimensional stability. It

has good electrical properties, wear resistance, chemical resistance,

dyeability, finished product processing and mechanical processing. ABS

resin is resistant to water, inorganic salts, alkali and acids, insoluble in

most alcohols and hydrocarbon solvents, but easily soluble in aldehydes,

ketones, esters and certain chlorinated hydrocarbons. ABS resin has a

low thermal deformation temperature, is flammable, and has poor heat

resistance. The melting temperature is 217~237℃, and the thermal

ZOTAdecomposition temperature is above 250℃. Many modified ABS

materials on the market today are doped with sprue materials and

recycled materials. As a result, the performance of the customer’s

molded products is not very stable.

（

1）Material properties

It has good comprehensive performance, high impact strength, chemical

stability and good electrical properties;

It has good weldability with 372 organic glass and can be made into

two-color plastic parts, and the surface can be chrome-plated and

spray-painted;

There are high impact resistance, high heat resistance, flame retardant,

reinforced, transparent and other grades;

The fluidity is slightly worse than HIPS, better than PMMA, PC, etc., and

has good flexibility;

Suitable for making general mechanical parts, wear-reducing and

wear-resistant parts, transmission parts and telecommunication parts.

(2) Molding performance

Amorphous materials, with medium fluidity and high moisture

absorption, must be fully dried. Plastic parts that require glossy surfaces

must be preheated and dried for a long time at 80-90 degrees for 3

hours;

It is advisable to have high material temperature and high mold

ZOTAtemperature, but if the material temperature is too high, it will easily

decompose (the decomposition temperature is >270°C). For

high-precision plastic parts, the mold temperature should be 50-60°C;

for high-gloss, heat-resistant plastic parts, the mold temperature should

be 60-80°C;

If you need to solve the water mark, you need to improve the fluidity of

the material, adopt methods such as high material temperature, high

mold temperature, or change the water inlet level;

If heat-resistant or flame-retardant materials are formed, plastic

decomposition will remain on the mold surface 3-7 days after

production, causing the mold surface to shine. The mold needs to be

cleaned in time, and an exhaust position needs to be added on the mold

surface;

The cooling speed is fast, the mold pouring system should be thick and

short as the principle, cold material cavity should be set up, and the gate

should be large, such as direct gate, disc gate or fan gate, etc., but the

internal stress should be prevented from increasing. , an adjustable gate

can be used if necessary. The mold should be heated and wear-resistant

steel should be used;

The material temperature has a great influence on the quality of plastic

parts. If the material temperature is too low, it will cause material

shortage, the surface is dull, and the silver wires are disordered. If the

ZOTAmaterial temperature is too high, it will easily overflow, dark stripes of

silver wire will appear, and the plastic parts will become discolored and

blistered;

Mold temperature has a great influence on the quality of plastic parts.

When the mold temperature is low, the shrinkage, elongation, and

impact strength are high, and the bending resistance, compression

resistance, and tensile strength are low. When the mold temperature

exceeds 120°C, the plastic parts cool slowly, are prone to deformation

and stick to the mold, are difficult to demould, and have a long molding

cycle;

The molding shrinkage is small, melt cracking is prone to occur, and

stress concentration occurs. Therefore, the molding conditions should be

strictly controlled during molding, and the plastic parts should be

annealed after molding;

The melting temperature is high, the viscosity is high, and it is not

sensitive to shearing. For plastic parts larger than 200 grams, a screw

injection machine should be used. The nozzle should be heated, and an

open extension nozzle should be used. The injection speed is medium to

high.

ZOTA

常用塑料的性能用途

Performance uses of commonly used plastics

PE 是聚乙烯塑料，化学性能稳定，通常制作食品袋及各种容器，耐酸、耐碱及盐类水溶液的侵蚀，但不宜

用强碱性洗涤剂擦拭或浸泡。

PE is polyethylene plastic with stable chemical properties. It is usually made into food bags and

various containers. It is resistant to acid, alkali and salt aqueous solutions, but it should not be

wiped or soaked with strong alkaline detergents.

PP 是聚丙烯塑料，无毒、无味，可在 100℃的沸水中浸泡不变形、不损伤，常见的酸、碱有机溶剂对它几

乎不起作用。多用于食具。

PP is polypropylene plastic, which is non-toxic and odorless. It can be soaked in boiling water at

100°C without deformation or damage. Common acid and alkali organic solvents have almost

no effect on it. Mostly used for tableware.

PS 是聚苯乙烯塑料，容易着色、透明性好，多用于制作灯罩、牙刷柄、玩具、电器零部件。它耐酸碱腐蚀，

但易溶于氯仿、二氯乙烯、香蕉水等有机溶剂。

PS is polystyrene plastic, which is easy to color and has good transparency. It is mostly used to

make lampshades, toothbrush handles, toys, and electrical components. It is resistant to acid and

alkali corrosion, but is easily soluble in organic solvents such as chloroform, dichloroethylene,

banana water, etc.

PVC 是聚氯乙烯塑料，色泽鲜艳、耐腐蚀、牢固耐用，由于在制造过程中增加了增塑剂、抗老化剂等一些

有毒辅助材料，故其产品一般不存放食品和药品。

PVC is polyvinyl chloride plastic, which is bright-colored, corrosion-resistant, strong and durable.

Due to the addition of some toxic auxiliary materials such as plasticizers and anti-aging agents

during the manufacturing process, its products generally do not store food and medicine.

ABS 是由丙烯腈、丁二烯、苯乙烯聚合的塑料，它色彩醒目，耐热、坚固、外表面可镀铬、镍等金属薄膜，

可制作琴键、按钮、刀架、电视机外壳、伞柄等。

ABS is a plastic polymerized by acrylonitrile, butadiene, and styrene. It has eye-catching colors,

heat resistance, and strength. The outer surface can be plated with chrome, nickel and other

metal films. It can be used to make piano keys, buttons, knife holders, TV casings, and umbrella

handles. wait.

PA 是尼龙塑料，它的特性坚韧、牢固、耐磨，常用于制作梳子、牙刷、衣钩、扇骨、网袋绳、水果外包装

袋等。无毒性，但不可长期与酸碱接触。

PA is a nylon plastic. It is tough, strong and wear-resistant. It is often used to make combs,

toothbrushes, clothes hooks, fan ribs, mesh bag ropes, fruit packaging bags, etc. Non-toxic, but

not in long-term contact with acids and alkalis.

ZOTA

PP 片材的使用性能有什么特性

What are the performance characteristics of PP sheets?

相信大对 pvc 片材或者 PP 片材你们都在市面上有很多的了解吧，今天我们讲讲

专用填充的 PP 片材有哪些性能使用？

I believe you all have a lot of knowledge about PVC sheets or PP sheets

on the market. Today we will talk about the properties of specially filled

PP sheets?

PP 片材产品特性：

PP sheet product characteristics:

1、PP 片材分散性好：与聚本稀，聚乙稀相容型优良，因此即使加入较大的填充

量，仍可获得外观光洁度很好的产品。

1. PP sheet has good dispersion: it has excellent compatibility with

polypropylene and polyethylene, so even if a larger filling amount is

added, a product with a good appearance can still be obtained.

2、PP 片材白度高：本产品为纯白色粒料，可灵活配制生产各种颜色制品。

2. PP sheet has high whiteness: This product is pure white pellets and

can be flexibly formulated to produce products of various colors.

3、使用偶联剂处理：在填充量大的情况下，使制品仍保持良好的机械性能。

3. Use coupling agent treatment: even if the filling amount is large, the

product can still maintain good mechanical properties.

4、工艺适应性广：可用原来的加工设备和工艺生产。

4. Wide process adaptability: original processing equipment and

ZOTAprocesses can be used for production.

PP 片材产品优势：

Advantages of PP sheet products:

1、降低制品的成本，提高生产效率，获得良好的经济效益。

1. Reduce the cost of products, improve production efficiency, and

obtain good economic benefits.

2、增强制品的刚性及增加制品的重量。

2. Enhance the rigidity of the product and increase the weight of the

product.

3、减少制品收缩性及收缩引起的变形。

3. Reduce product shrinkage and deformation caused by shrinkage.

产品用途：

Product Usage:

PP 片材专门用于流延膜，打孔膜制品以及相关产品的复合生产，PP 片材以及聚

乙烯各种制品的生产（包括吹膜 打孔膜 流延膜 农用膜 大棚膜等）。

PP sheet is specially used for the composite production of cast film,

perforated film products and related products, the production of PP

sheet and various polyethylene products (including blown film,

perforated film, cast film, agricultural film, greenhouse film, etc.).

ZOTA

PC 片材有哪些优越性能

What are the superior properties of PC sheets?

关于 PC 片材的优越性能，主要是：

Regarding the superior properties of PC sheets, the main ones are:

一、具有良好的耐热性达 125 度和耐低温性零下 45 度，在较宽的温度范围内具有稳定的力学性能，尺寸

稳定性，电性能和阻燃性，可在-60~120℃下长期使用；无明显熔点，在 220-230℃呈熔融状态；由于分

子链刚性大，树脂熔体粘度大；

1. It has good heat resistance up to 125 degrees and low temperature resistance of minus 45

degrees. It has stable mechanical properties, dimensional stability, electrical properties and flame

retardancy in a wide temperature range, and can be used at -60~120℃ It has no obvious melting

point and is in a molten state at 220-230℃; due to the high rigidity of the molecular chain, the

resin melt viscosity is high;

二、对光稳定，但不耐紫外光，耐候性好；耐油、耐酸、不耐强碱、氧化性酸及胺、酮类，溶于氯化烃类

和芳香族溶剂，长期在水中易引起水解和开裂，缺点是因抗疲劳强度差，容易产生应力开裂，抗溶剂性差，

耐磨性欠佳。

2. Stable to light, but not resistant to ultraviolet light, good weather resistance; resistant to oil,

acid, strong alkali, oxidizing acids, amines, and ketones. It is soluble in chlorinated hydrocarbons

and aromatic solvents, and can easily cause damage when exposed to water for a long time.

Hydrolysis and cracking, the disadvantages are that it is prone to stress cracking due to poor

fatigue resistance, poor solvent resistance, and poor wear resistance.

三、耐冲击性优异，拉伸强度、弯曲强度、压缩强度高；蠕变性小，尺寸稳定。

3. Excellent impact resistance, high tensile strength, bending strength and compressive strength;

small creep property and stable dimensions.

四、吸水率小，收缩率小，尺寸精度高，尺寸稳定性好，薄膜透气性小；属自熄性材料；

4. Low water absorption, small shrinkage, high dimensional accuracy, good dimensional stability,

low film permeability; it is a self-extinguishing material;

五、具有优良的物理机械性能。

5. It has excellent physical and mechanical properties.

ZOTA

PE 片材用什么胶水、黏胶剂粘合？

What glue and adhesive are used to bond PE sheets?

可用 3M 结构胶 DP-8005 或 DP-8010，热熔胶 3731, 3748, 3764

Available 3M structure is DP-8005 or DP-8010, hot melt adhesive 3731,

3748, 3764

ZOTA

PE 片材暴晒后会怎么样？

What will happen to PE sheets after they are exposed to the sun?

变黄。然后裂解。但不会降解。

Turn yellow. Then lyse. But it won’t degrade.

因为里面的分子链会被紫外线破坏断裂变脆弱。同时，一部分会被氧化，所以变

黄。

Because the molecular chains inside will be damaged by ultraviolet rays

and become fragile. At the same time, part of it will be oxidized and turn

yellow.

如果希望延缓变黄变脆现象，可以加入抗紫外线剂。

If you want to delay yellowing and brittleness, you can add an anti-UV

agent.

扬州卓泰新材料有限公司主要产品:PE 片材|pe 片材|PE 吸塑片材等。

The main products of Yangzhou Zhuotai New Materials Co., Ltd. are:

PE sheets | PE sheets | PE blister sheets, etc.

ZOTA